TPU烟台美瑞E190L原料粒子介绍

总体  
材料状态  •已商用：当前有效
 
资料 1  •Brochure - Product description (Japanese)
 •Processing (Japanese)
 •Technical Datasheet - data table (Japanese)
 
 
供货地区  •亚太地区
 
性能特点  •减震
•抗撞击性，良好
•良好的强度
•良好的柔韧性
 •良好的撕裂强度
•耐臭氧性能
•耐低温
•耐化学性良好
 •耐磨损性良好
•耐气候影响性能良好
•耐油性能
 
 

物理性能 额定值 单位制 测试方法
比重 1.22 g/cm³ ASTM D792
硬度 额定值 单位制 测试方法
硬度计硬度 (邵氏 A, 23°C, 2.00 mm, 注塑) 88 到 92   ASTM D2240

机械性能 额定值 单位制 测试方法
抗泰伯磨耗 (23°C, 1000 Cycles, 1000 g, H-22 转轮) 35.0 mg ASTM D1044
弹性体 额定值 单位制 测试方法
拉伸应力 2 (100%应变, 23°C, 2.00 mm) 10.0 MPa ASTM D412
抗张强度 2 (屈服, 23°C, 2.00 mm) 46.0 MPa ASTM D412
伸长率 2 (断裂, 23°C, 2.00 mm) 580 % ASTM D412
撕裂强度 2 (23°C, 2.00 mm) 137 kN/m ASTM D624
压缩永久变形 (70°C, 22.0 hr) 32 % ASTM D395
Rebound Resilience (23°C, 2.00 mm) 45 %  

热性能 额定值 单位制 测试方法
玻璃转化温度(DSC) -43.0 °C DSC
维卡软化温度 118 °C ASTM D1525 3

补充信息
Test Methods: JIS K7311, K6262, K7206

General  
Material Status  •Commercial: Active

Availability  •Asia Pacific
 
Features  •Good Chemical Resistance
•Good Flexibility
•Good Impact Resistance
•Good Strength
 •Good Tear Strength
•Good Wear Resistance
•Good Weather Resistance
•Low Temperature Resistant
 •Oil Resistant
•Ozone Resistant
•Vibration Damping
 

Physical Nominal Value Unit Test Method
Specific Gravity 1.22 g/cm³ ASTM D792
Hardness Nominal Value Unit Test Method
Durometer Hardness (Shore A, 23°C, 2.00 mm, Injection Molded) 88 to 92   ASTM D2240

Mechanical Nominal Value Unit Test Method
Taber Abrasion Resistance (23°C, 1000 Cycles, 1000 g, H-22 Wheel) 35.0 mg ASTM D1044
Elastomers Nominal Value Unit Test Method
Tensile Stress 2 (100% Strain, 23°C, 2.00 mm) 10.0 MPa ASTM D412
Tensile Strength 2 (Yield, 23°C, 2.00 mm) 46.0 MPa ASTM D412
Tensile Elongation 2 (Break, 23°C, 2.00 mm) 580 % ASTM D412
Tear Strength 2 (23°C, 2.00 mm) 137 kN/m ASTM D624
Compression Set (70°C, 22.0 hr) 32 % ASTM D395
Rebound Resilience (23°C, 2.00 mm) 45 %  

Thermal Nominal Value Unit Test Method
Glass Transition Temperature (DSC) -43.0 °C DSC
Vicat Softening Temperature 118 °C ASTM D1525 3

Additional Information
Test Methods: JIS K7311, K6262, K7206